Akro-Plastic Akromid® S3 GF 50 1 (3533) PA 6.10 Dry, 50% Glass Filled

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® S3 GF 50 1 (3533) PA 6.10 Dry, 50% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw material used is sebacic acid, synthesized from castor oil which is obtained from the seeds of Ricinus communis, the castor oil plant. From a technical standpoint, AKROMID® S closes the gap between PA 6/PA 6.6 and PA 12. It is characterized by significantly lower moisture absorption compared to PA 6 and PA 6.6. At 23 °C and 50 % relative humidity, typical values for these product types are 3 % and 2.8 %, respectively. With a value of approximately 1.4 %, PA 6.10 absorbs just half as much moisture and can therefore be used as an engineering material in applications requiring a high dimensional consistency. Moreover, it exhibits excellent cold impact resistance. Other outstanding characteristics include very good chemical resistance due to the structure of the polymer and high hydrolysis resistance, although it can be processed like all common polyamides. The materials from the PA 6.10 product family are further characterized by exceptional dimensional stability, good surface resistance, good abrasion resistance and wear behaviour, and an improved carbon footprint. This is due to the fact that the plant-based raw materials have already removed CO2 from the environment during their growth phase. The product portfolio currently comprises one non reinforced variant and several reinforced variants with a glass-fibre content ranging from 15 % to 50 %. AKROMID® S is a bioplastic according to today’s standards. Unlike certain materials used in the packaging industry, however, the material is not biodegradable. The distinguishing feature of AKROMID® S is its reduced ecological footprint: The use of harmful CO2 per ton of polyamide produced from renewable resources is significantly lower compared to one ton produced from fossil-based resources, without affecting the product’s performance characteristics.Applications:Automotive SectorConnectors and housingsNon-return valvesPower steering-fluid reservoirsCorrugated tubing and fluid pipesMachine Construction and Tool-BuildingGearsDoor handles and fittingsOffice equipment, housings, functional parts, amongst othersConnectors and plugsPower toolsSports and LeisureComponents in high-end garden toolsBicycle accessoriesSail-boat accessoriesWinter sports accessoriesInformation from Akro-Plastic
Physical Properties Metric English Comments
Density 1.51 g/cc

@Temperature 23.0 °C
0.0546 lb/in³

@Temperature 73.4 °F
ISO 1183
Filler Content 50 %
50 %
ISO 1172
Water Absorption 0.90 %

@Temperature 70.0 °C
0.90 %

@Temperature 158 °F
62% r.h., Humdity; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 25.0 °C,
Treatment Temp. 70.0 °C
0.35 %

@Temperature 77.0 °F,
Treatment Temp. 158 °F
62% rel. humidity
0.40 %

@Temperature 50.0 °C,
Treatment Temp. 70.0 °C
0.40 %

@Temperature 122 °F,
Treatment Temp. 158 °F
62% rel. humidity
0.60 %

@Treatment Temp. 70.0 °C,
Temperature 145 °C
0.60 %

@Treatment Temp. 158 °F,
Temperature 293 °F
62% rel. humidity
0.70 %

@Treatment Temp. 70.0 °C,
Temperature 310 °C
0.70 %

@Treatment Temp. 158 °F,
Temperature 590 °F
62% rel. humidity
0.70 %

@Treatment Temp. 70.0 °C,
Temperature 335 °C
0.70 %

@Treatment Temp. 158 °F,
Temperature 635 °F
62% rel. humidity
0.75 %

@Treatment Temp. 70.0 °C,
Temperature 220 °C
0.75 %

@Treatment Temp. 158 °F,
Temperature 428 °F
62% rel. humidity
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4
Spiral Flow 35.0 cm
13.8 in
AKRO
Mechanical Properties Metric English Comments
Ball Indentation Hardness 230 MPa
33400 psi
H 961/30; ISO 2039-1
Tensile Strength at Break 200 MPa
29000 psi
5 [mm/min]; ISO 527-1/2
Elongation at Break 3.5 %
3.5 %
5 [mm/min]; ISO 527-1/2
3.6 %
3.6 %
Flexural Strain, 2 [mm/min]; ISO 178
Tensile Modulus 14.5 GPa
2100 ksi
1[mm/min]; ISO 527-1/2
10.5 GPa

@Treatment Temp. 70.0 °C,
Time 1.22e+6 sec
1520 ksi

@Treatment Temp. 158 °F,
Time 340 hour
62% rel. humidity
10.8 GPa

@Treatment Temp. 70.0 °C,
Time 1.15e+6 sec
1570 ksi

@Treatment Temp. 158 °F,
Time 320 hour
62% rel. humidity
11.0 GPa

@Treatment Temp. 70.0 °C,
Time 936000 sec
1600 ksi

@Treatment Temp. 158 °F,
Time 260 hour
62% rel. humidity
11.5 GPa

@Treatment Temp. 70.0 °C,
Time 522000 sec
1670 ksi

@Treatment Temp. 158 °F,
Time 145 hour
62% rel. humidity
12.4 GPa

@Treatment Temp. 70.0 °C,
Time 180000 sec
1800 ksi

@Treatment Temp. 158 °F,
Time 50.0 hour
62% rel. humidity
12.5 GPa

@Treatment Temp. 70.0 °C,
Time 90000 sec
1810 ksi

@Treatment Temp. 158 °F,
Time 25.0 hour
62% rel. humidity
Flexural Strength 310 MPa
45000 psi
2 [mm/min]; ISO 178
Flexural Modulus 13.8 GPa
2000 ksi
2 [mm/min]; ISO 178
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
10.5 J/cm²

@Temperature -30.0 °C
50.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 11357-1, DSC,10 [K/min]
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
HDT/A; ISO 75-1/2
Deflection Temperature at 8.0 MPa 170 °C
338 °F
HDT/C; ISO 75-1/2
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Processing Properties Metric English Comments
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Nozzle Temperature 240 - 295 °C
464 - 563 °F
Zone 1 220 - 300 °C
428 - 572 °F
Zone 2 220 - 300 °C
428 - 572 °F
Zone 3 220 - 300 °C
428 - 572 °F
Zone 4 220 - 300 °C
428 - 572 °F
Melt Temperature 260 - 310 °C
500 - 590 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time <= 4 hour
<= 4 hour
Hold Pressure 30.0 - 80.0 MPa
4350 - 11600 psi
Back Pressure 5.00 - 15.0 MPa
725 - 2180 psi
Descriptive Properties Value Comments
Rate acc. FMVSS 302 ( Passed
Rate acc. FMVSS 302,( FMVSS 302, >1 [mm] Thickness