Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 % @Time 86400 sec |
0.70 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527-1/-2 |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527-1/-2 |
| Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-1/-2 |
| Flexural Strength | 265 MPa | 38400 psi | ISO 178 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
| Charpy Impact Unnotched | 9.30 J/cm² | 44.3 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.0 µm/m-°C | 12.2 µin/in-°F | ISO 11359-2 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP CZL36 PS
- Techmer ES Electrafil® ABS-1251/SD ABS, Static Dissipative Polymer Alloy
- Samsung Cheil Industries Starex® SR-0310FM ABS, Unreinforced Heat Resistant
- Teknor Apex Laripur® LPR 9060EM Thermoplastic Polyurethane
- ThyssenKrupp XAR® 500 Structural Steel
- Dynasol Solprene® 233P Polybutadiene Rubber
- ATI Allvac® Nickelvac® 800 & 800-H UNS N08800 & UNS N08810 Nickel Superalloy
- Latrobe Lescalloy® AF 1410 VIM-VAR ; 6 in High Strength Alloy Steel
- Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F)
Copyright © lookpolymers.com All Rights Reserved