- Polymer Property : Tensile Modulus = 0.900 GPa
Polymer Property : Tensile Modulus = 0.900 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 0.900 GPa | 131 ksi | STN EN ISO 527-2 |
| Plastcom SLOVALEN PQ 91 N Polypropylene Homopolymer, Modified with Elastomer, Impacted FeaturesHomopolymer PP modified with elastomer. The addition of thermoplastic elastomer causes increased toughness, possible alternative to PP copolymers. General application in all industry branc.. |
|||
| Tensile Modulus | >= 0.900 GPa | >= 131 ksi | 2% sec, MD; ASTM D882 |
| NIZHNEKAMSKNEFTEKHIM PE 4252A (524H1) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1 mm/min; ISO 527-1,-2 |
| Inno-Comp INNOPOL® CS 2-2000 TO Polypropylene Block-Copolymer Based Compound INNOPOL® CS 2-2000 TO is a polypropylene block-copolymer based compound. This grade is available in natural and custom colored form.INNOPOL® CS 2-2000 TO is developed for producing injection m.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1 mm/min; ISO 527-1,-2 |
| Inno-Comp INNOPOL® CS 2-3302 Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-3302 is an elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-3302 is developed for produ.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | |
| LATI Laticonther 83 CP/85 PA12, Impact Modified High thermal conductivity product based on Polyamide 12 (PA12), impact modified. Special filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation prov.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 Type 1A |
| Solvay TECHNYL® B 230 PA66/6, Conditioned Description: Unreinforced and modified copolyamide 66/6, with high flexibility and improved impact resistance, for injection molding.Available in: Asia Pacific and EuropeProduct Applications: TECHN.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 Type 1A |
| Solvay TECHNYL® B 238 Black 21 N PA66/6, Conditioned Description: Unreinforced and modified copolyamide 66/6, heat stabilized, with improved impact resistance, for injection molding.Available in: EuropeProduct Applications: TECHNYL B 238 is particular.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 Type 1A |
| Solvay TECHNYL® C 442 Black V PA6, DRY Description: Unreinforced polyamide PA6, high viscosity, with high flexibility and very high impact resistance even at low temperature, for extrusion.Available in: Europe Product Applications: It ha.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 Type 1A |
| Solvay TECHNYL® C 502XT PA6, Conditioned Description: Unreinforced polyamide 6, very high viscosity, for extrusion.Available in: Europe Product Applications: It is suitable for extruded semi-finished products, such as: Rods, profiles, shee.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp TH0450D PUR (Asia Pacific) LNP* Thermocomp* TH0450D is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by .. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527-2 |
| Borealis Borpact™ SG910MO Polypropylene for Injection Molding Borpact™ SG910MO is a high impact and transparent polypropylene. This grade provides high gloss, high transparency and excellent impact properties. Applications: containers and products with medium.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527-2 |
| Borealis BorPURE™ MB6562 High Density Polyethylene for Injection Molding BorPure™ MB6562 is a bimodal, high-density polyethylene intended for injection and compression molding. This grade combines excellent organoleptic properties, environmental stress crack resistance .. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527-2 |
| Borealis Daploy™ WB260HMS Polypropylene Daploy™ WB260HMS is a propylene-based, structurally isomeric polymer. Applications: cushioning and protective packaging, door liners, lightweight packaging trays, beakers and containers, microwave.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527 |
| Borealis RA130E Polypropylene Random Copolymer RA130E is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is natural colored. Applications RA130E is recommended for the production of PP-R pipes and .. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527 |
| Borealis RA130E-6017 Polypropylene Random Copolymer RA130E-6017 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and indust.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527 |
| Borealis RA130E-6034 Polypropylene Random Copolymer RA130E-6034 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and indust.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527-2 |
| Borealis RB307MO Polypropylene Random Copolymer RB307MO is a random copolymer with good transparency and contact clarity, very good gloss and surface finish. This grade also features high heat distortion temperature. Applications: household and.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527 |
| Borealis RA130E-2492 Polypropylene Random Copolymer RA130E-2492 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is dark blue colored. Applications: domestic water, heating, relining, plumbing, and in.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527 |
| Borealis RA130E-8427 Polypropylene Random Copolymer RA130E-8427 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is grey colored. Applications: domestic water, heating, relining, plumbing, and industr.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527-1/-2 |
| DSM Arnitel® EM740 Polyether Ester Elastomer (European Grade) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | cond; ISO 527-1/-2 |
| DSM EcoPaXX® Q-E7300 PA410-I Tube Extrusion |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BZ 1/2 PA6 Product description: Grilon BZ 1/2 is an unreinforced, impact modified PA6 injection molding grade with normal melt viscosity. Grilon BZ 1/2 has the following important properties: Good flow behavio.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 |
| CP-Polymer-Technik Wellamid® 6000/58 CP Nylon 6, Impact Modified Until -40°C, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® ST801 NC010A Nylon 66
(Unverified Data**) Super Toughened Polyamide 6 Zytel ST801 is an unreinforced super tough polyamide 66 for injection molding and extrusion. It offers outstanding break resistance over a wide temperature and humidity r.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | ASTM D638 |
| Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (10 mm Molded Thickness) AZDEL SuperLite® SL551800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | |
| BASF Novolen® 2700 L Polypropylene UV stabilized grade for injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | |
| BASF Novolen® 3200 MC Polypropylene Cast film without slip and blocking agents.Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | cond.; ISO 527 |
| Azoty Tarnow™ Tarnamid® T-27 MHLS Polyamide 6 - Colored Heat and UV light stabilized grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main proper.. |
|||
| Tensile Modulus | 0.900 GPa @Temperature 23.0 °C |
131 ksi @Temperature 73.4 °F |
ISO 527 |
| DuPont Performance Polymers Hytrel® HTR8539 BK316 TPC-ET
(Unverified Data**) Hytrel® HTR8539 is a 72 Shore D, plasticiser free, high performance resin for extrusion. It has high viscosity.Information provided by DuPont Performance Polymers |
|||
| Tensile Modulus | 0.900 GPa | 131 ksi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BZ 1 PA6 Information provided by EMS Grivory |
|||