SABIC Innovative Plastics LNP Thermocomp TH0450D PUR (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp TH0450D PUR (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* TH0450D is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.50 g/cc | 0.163 lb/in³ | ASTM D 792 |
| 4.50 g/cc | 0.163 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0064 cm/cm @Time 86400 sec |
0.0064 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
| 22.0 MPa | 3190 psi | ISO 527 | |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D 638 |
| 22.0 MPa | 3190 psi | ISO 527 | |
| Elongation at Break | 52.8 % | 52.8 % | ISO 527 |
| 61.2 % | 61.2 % | ASTM D 638 | |
| Elongation at Yield | 44.7 % | 44.7 % | ISO 527 |
| 48 % | 48 % | ASTM D 638 | |
| Tensile Modulus | 0.900 GPa | 131 ksi | 1 mm/min; ISO 527 |
| 1.18 GPa | 171 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 13.0 MPa | 1890 psi | ASTM D 790 |
| 19.0 MPa | 2760 psi | ISO 178 | |
| Flexural Modulus | 0.870 GPa | 126 ksi | ASTM D 790 |
| 0.870 GPa | 126 ksi | ISO 178 | |
| Izod Impact, Notched | 1.92 J/cm @Temperature 23.0 °C |
3.60 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 21.84 J/cm @Temperature 23.0 °C |
40.92 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 155 kJ/m² @Temperature 23.0 °C |
73.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 20.0 J | 14.8 ft-lb | Multiaxial Impact; ISO 6603 |
| 19.0 J @Temperature 23.0 °C |
14.0 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 89.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 82.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 84.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 41.0 °C @Thickness 3.20 mm |
106 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- LyondellBasell Lupolen® 2420 F LDPE
- Global PP-1102-K Polypropylene Homopolymer
- Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, As Conditioned
- Sibur L-85M Polyvinyl Chloride (PVC)
- Saint-Gobain Norton® V730 Pressure Sensitive Adhesive Sealant Foam
- Tra-Con Tra-Bond 872-7TN1 Flexible Thixotropic Epoxy Adhesive
- Epoxy Technology EPO-TEK® OG142 UV Cure Optical Epoxy
- Resirene Resirene® 6110 High Impact Polystyrene