Borealis RA130E-6034 Polypropylene Random Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Borealis
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis RA130E-6034 Polypropylene Random Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

RA130E-6034 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and industrial applications. Specifications: DIN 8078; DIN 8077; and EN ISO 15874.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ISO 1183
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.0 MPa	3630 psi	50mm/min; ISO 527-2
Elongation at Yield	13.5 %	13.5 %	50mm/min; ISO 527-2
Tensile Modulus	0.900 GPa	131 ksi	1mm/min; ISO 527
Flexural Modulus	0.800 GPa	116 ksi	2mm/min; ISO 178
Charpy Impact Unnotched	4.00 J/cm² @Temperature -20.0 °C	19.0 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
	NB @Temperature 0.000 °C	NB @Temperature 32.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.200 J/cm² @Temperature -20.0 °C	0.952 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	0.350 J/cm² @Temperature 0.000 °C	1.67 ft-lb/in² @Temperature 32.0 °F	ISO 179/1eA
	2.00 J/cm² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	150 µm/m-°C @Temperature 0.000 - 70.0 °C	83.3 µin/in-°F @Temperature 32.0 - 158 °F	DIN 53752
Thermal Conductivity	0.240 W/m-K	1.67 BTU-in/hr-ft²-°F	DIN 52612

Processing Properties	Metric	English	Comments
Middle Barrel Temperature	180 - 210 °C	356 - 410 °F	cylinder
Die Temperature	210 - 220 °C	410 - 428 °F
Melt Temperature	220 °C	428 °F
Head Temperature	210 - 220 °C	410 - 428 °F