Material Notes:

Cast film without slip and blocking agents.Data was collected by ISO methods and provided by BASF.

Physical Properties	Metric	English	Comments
Density	0.910 g/cc	0.0329 lb/in³
Water Absorption	0.10 %	0.10 %
Moisture Absorption at Equilibrium	0.10 %	0.10 %
Melt Flow	11 g/10 min @Load 2.16 kg, Temperature 230 °C	11 g/10 min @Load 4.76 lb, Temperature 446 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.0 MPa	3630 psi
Elongation at Break	>= 50 %	>= 50 %
Elongation at Yield	11 %	11 %
Tensile Modulus	0.900 GPa	131 ksi
Charpy Impact Unnotched	NB	NB
	1.60 J/cm² @Temperature -30.0 °C	7.61 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²
	0.150 J/cm² @Temperature -30.0 °C	0.714 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	185 µm/m-°C @Temperature 20.0 °C	103 µin/in-°F @Temperature 68.0 °F
Melting Point	145 °C	293 °F
Deflection Temperature at 0.46 MPa (66 psi)	68.0 °C	154 °F
Deflection Temperature at 1.8 MPa (264 psi)	47.0 °C	117 °F
Vicat Softening Point	72.0 °C	162 °F

Electrical Properties	Metric	English	Comments
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.3 @Frequency 1e+6 Hz	2.3 @Frequency 1e+6 Hz
Dielectric Strength	140 kV/mm	3560 kV/in
Dissipation Factor	0.000070 @Frequency 100 Hz	0.000070 @Frequency 100 Hz
	0.00020 @Frequency 1e+6 Hz	0.00020 @Frequency 1e+6 Hz
Comparative Tracking Index	600 V	600 V