Plastcom SLOVALEN PQ 91 N Polypropylene Homopolymer, Modified with Elastomer, Impacted

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Plastcom spol. s r.o.
Trade Name	SLOVALEN
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom SLOVALEN PQ 91 N Polypropylene Homopolymer, Modified with Elastomer, Impacted.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FeaturesHomopolymer PP modified with elastomer. The addition of thermoplastic elastomer causes increased toughness, possible alternative to PP copolymers. General application in all industry branches - packing material, garden flower-pots, toys, furniture industry, hinges, fasteners, clamps, office chairs, hangers etc. Delivered in natural and in the full RAL color scale. Shows higher toughness and MFI in comparison with PQ 51 N.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	0.880 g/cc	0.0318 lb/in³	STN 64 0111
Linear Mold Shrinkage	0.019 cm/cm	0.019 in/in	STN 64 0808
Linear Mold Shrinkage, Transverse	0.0195 cm/cm	0.0195 in/in	STN 64 0808
Melt Flow	25 g/10 min @Load 2.16 kg, Temperature 230 °C	25 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	25.0 MPa	3630 psi	STN EN ISO 527-2
Elongation at Break	300 %	300 %	STN EN ISO 527-2
Tensile Modulus	0.900 GPa	131 ksi	STN EN ISO 527-2
Flexural Strength	20.0 MPa	2900 psi	STN EN ISO 178
Flexural Modulus	0.700 GPa	102 ksi	STN EN ISO 178
Charpy Impact Unnotched	7.50 J/cm² @Temperature -20.0 °C	35.7 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	STN EN ISO 179
Charpy Impact, Notched	0.700 J/cm² @Temperature -20.0 °C	3.33 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	1.00 J/cm² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	140 °C	284 °F	DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	STN EN ISO 75/A
Vicat Softening Point	115 °C	239 °F	B; STN EN ISO 306

Processing Properties	Metric	English
Melt Temperature	200 - 250 °C	392 - 482 °F
Mold Temperature	30.0 - 50.0 °C	86.0 - 122 °F
Injection Pressure	60.0 - 70.0 MPa	8700 - 10200 psi