| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BZ 1 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Water Absorption | 9.0 % | 9.0 % | ISO 62 |
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | conditioned; ISO 2039-1 |
| 110 MPa | 16000 psi | dry; ISO 2039-1 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
| 65.0 MPa | 9430 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 25 % | 25 % | dry; ISO 527-1/-2 |
| 25 % | 25 % | dry; ISO 527-1/-2 | |
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.900 GPa | 131 ksi | conditioned; ISO 527-1/-2 |
| 2.40 GPa | 348 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
| NB | NB | conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA |
| 3.00 J/cm² | 14.3 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| 0.800 J/cm² @Temperature 30.0 °C |
3.81 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 70.0 - 90.0 °C | 158 - 194 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | conditioned; IEC 60243-1 |
| 33.0 kV/mm | 838 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
| 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Connectors | |
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY6012 PC+ABS (Asia Pacific)
- LG Chemical LUMID GP2500B(W) PA66+GF50%, General Purpose
- H.C. Starck Amperit® 704.092 Chromium Oxide (Cr2O3) 99.5%
- Stir SpA LG 57 AT 1 (PVC)
- SABIC Innovative Plastics LNP THERMOCOMP RF0079SZ PA 66 (Asia Pacific)
- Teknor Apex Synres® PP G10 17 Polypropylene, Glass Reinforced
- Westlake Plastics Lennite® GUR1020 (Type I) Ultra-high Molecular Weight Polyethylene For Medical Applications
- Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction
- Arlon 0.015" (0.381 mm) Flexible Heater Silicone with Fiberglass Substrate (51576R015)
Copyright © lookpolymers.com All Rights Reserved