NIZHNEKAMSKNEFTEKHIM PE 4252A (524H1) High Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 4252A (524H1) High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 - 0.954 g/cc | 0.0343 - 0.0345 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 0.10 - 0.20 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.10 - 0.20 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM D1283/L |
| 2.0 - 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
2.0 - 4.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@5kg ratio < 20; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 55.0 MPa | >= 7980 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 45.0 MPa | >= 6530 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 470 % | >= 470 % | ASTM D882 |
| Film Elongation at Break, TD | >= 570 % | >= 570 % | ASTM D882 |
| Tensile Modulus | >= 0.800 GPa | >= 116 ksi | 2% sec, TD; ASTM D882 |
| >= 0.900 GPa | >= 131 ksi | 2% sec, MD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 0.433 g/micron | >= 11.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 2.56 g/micron | >= 65.0 g/mil | ASTM D1922 |
| Dart Drop Test | >= 170 g | >= 0.375 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 600 |
Users viewing this material also viewed the following:
- LG Chemical HI121U ABS
- LATI Latigray 82-04 CX/90 PA 12
- Polyplastics Duranex® CN7030 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%, 30% GF filled
- Tisan TISLAMID® 66 Flame Retardant (V0). Halogen Free Heat Stabilized Nylon 66
- ChevronTexaco HD Soluble Oil
- ExxonMobil SpectraSyn Elite™ 150 Metallocene Polyalphaolefin (mPAO) Fluid
- Ascend Performance Materials VYDYNE® R400G Nylon, Mineral and Glass Reinforced
- BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Axiall SP-6235 Rigid PVC, Molding
Copyright © lookpolymers.com All Rights Reserved