Inno-Comp INNOPOL® CS 2-2000 TO Polypropylene Block-Copolymer Based Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-2000 TO Polypropylene Block-Copolymer Based Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-2000 TO is a polypropylene block-copolymer based compound. This grade is available in natural and custom colored form.INNOPOL® CS 2-2000 TO is developed for producing injection molded automotive components, where the required properties are good stiffness and processability besides excellent low-temperature impact resistance.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc @Temperature 23.0 °C |
0.0325 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 0.30 % @Temperature 600 °C |
0.30 % @Temperature 1110 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 0.900 GPa | 131 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 0.950 GPa | 138 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1,-2 |
| Vicat Softening Point | 56.0 °C | 133 °F | B120; ISO 306 |
| 135 °C | 275 °F | A120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |
Users viewing this material also viewed the following:
- Murtfeldt Material ”S”® 1000 Black Antistatic Polyethylene, Conductive
- SABIC Innovative Plastics Lexan® 925AU PC
- DSM Akulon® K224-HG5 Nylon 6-25% Glass Reinforced (European and Asian Grade) (Dry) (discontinued **)
- Karina 651-48/1-BY-IS Black PVC Compound
- Styron XZ 95047.00 Carboxylated SB
- EMS-Grivory Grivory® HB5299 PA*
- Axion Polymers Axpoly® PS02 Impact Modified Polystyrene
- 3M Scotchcast™ 2136 Potting Kit
- Bhansali Engineering Abstron HR-60 ABS Heat Resistant
- Carlisle 201LD Carbon-Carbon Composite
Copyright © lookpolymers.com All Rights Reserved