- DSM EcoPaXX® Q-E7300 PA410-I
DSM EcoPaXX® Q-E7300 PA410-I
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-E7300 PA410-I.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tube Extrusion
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.70 % | 1.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.028 cm/cm | 0.028 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | cond; ISO 527-1/-2 |
| 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 30 % | 30 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Elongation at Yield | 6.0 % | 6.0 % | dry; ISO 527-1/-2 |
| 20 % | 20 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 0.900 GPa | 131 ksi | cond; ISO 527-1/-2 |
| 1.80 GPa | 261 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 40.0 MPa | 5800 psi | cond; ISO 178 |
| 70.0 MPa | 10200 psi | dry; ISO 178 | |
| Flexural Modulus | 0.950 GPa | 138 ksi | cond; ISO 178 |
| 1.75 GPa | 254 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C | 77.8 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | dry; ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 56 | ASTM 6866 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® RCY6713 PC (Asia Pacific)
- Plastcom SLOVALEN PH 69 GF 30 LS PP, 30% glass fibre, mod. of mech. prop., UV stability
- PolyOne LubriOne™ NJ-30CF/15T-2S Nylon 12 (discontinued **)
- Kazanorgsintez PE80B-285SL High Density Polyethylene Composite, Film Grade
- Mateck Neodymium Gallate Substrate, NdGaO3
- Polyplastics Duranex® 7400W Polybutylene Terephthalate (PBT), Super low warpage, GF filled
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N990 Filler
- DuPont Performance Polymers Zytel® RS 3061HSL BK039A Nylon 610 (Unverified Data**)
- Arlon R34696R026 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics Lexan® FL1000 PC
Copyright © lookpolymers.com All Rights Reserved