- Polymer Property : Tensile Strength at Break = 6960 psi
Polymer Property : Tensile Strength at Break = 6960 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CX7510 PC+ABS (Europe-Africa-Middle East) Cycoloy* CX7510 resin is an injection moldable, flame retardant PC/ABS blend, with non-chlorinated & non-brominated flame retardants. Key features of Cycoloy CX7510 resin include high heat, high flo.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat.. |
|||
| Tensile Strength at Break | <= 48.0 MPa | <= 6960 psi | ISO/R527 |
| Polykemi AB SCANBLEND FS8 FR UV PC/ASA, Flame Retardant, UV-Stabilized Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527-1,2 |
| Qualchem Danamid FEWLX2-25 Polyamide 6, 25% Mineral Filled Filled with minerals. Flame retardant, halogen-free (V-2)Information provided by Qualchem Zrt. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 505R PC (Asia Pacific) Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm... |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ISO 527-2 |
| Pasargad Polymer Peyvand Pasalac 3P-H9000B ABS/PC Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer (Asia Pacific) PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® DMX6014 PC Copolymer (Asia Pacific) DMX6014 is an injection moldable PC copolymer ABS blend. This resin combines excellent scratch resistance (F-pencil hardness) with ductility.This data was supplied by SABIC-IP for the Asia Pacific r.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HFD4271 PC Lexan* HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271 has enhanced mold release, impact ductility.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP GX07409H PSU LNP* LUBRICOMP* GX07409H is a compound based on PSU resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer LNP LUBRICOMP* KL003 is a compound based on Acetal Copolymer resin containing 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon LNP* LUBRICOMP* VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Stat-kon TE002 LNP* Stat-kon* TE002 is a compound based on Polyurethane resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the A.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ISO 527-2/50 |
| Styron CALIBREâ„¢ 301-58 LT Polycarbonate Resin Overview: CALIBREâ„¢ 301-58 LT is a high light transmission, high-flow polycarbonate resin for injection molding applications.Main Characteristics:High light transmissionHigh flow for injection m.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX NX0031 PPE+PA NORYL GTX* NX0031 resin is a conductive resin specially designed for electrostatic painting and powder coating applications. This material combines high impact, good flow and conductivity. The mate.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL N850 PPE+PS (Asia Pacific) ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical and Business Equipment applications. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PN275F PPE+PS PPE+PS with low mineral loading. High heat, platable applications. NSF approved for water contact applications. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 357U PBT+PC Unreinforced PC/PBT, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp KB002 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KB002 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP MX88028 PP (Asia Pacific) LNP* Thermocomp* MX88028 is a compound based on Polypropylene resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 2 in/min; ASTM D638 |
| A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ISO 527-2 |
| Total PSC 1160/1160N Crystal Polystyrene 1160 is a high resistance, high molecular weight crystal polystyrene mainly for the extrusion industry. Most notable for the production of bi-oriented polystyrene (BOPS). It is particularly useful.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D 638 |
| Cossa Polimeri ESTABLEND 4500 V0 HF Flame Retardant PC - ABS PC - ABS BlendFlame retardant class V0, chlorine and bromine free, good light resistance, excellent mechanical properties, excellent processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ISO 527-1/-2 |
| Covestro Desmopan® W DP 89051D Polyurethane PreprocessingMax. Water content |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0437G30CL Glass Reinforced Coupled |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | type I; ASTM D638 |
| BLUESTAR LXS 109 PPE-PS Typical Applications: Electrical partsFire RatedInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | XY direction; ASTM D638 |
| ALM PA 860 White Nylon 11 SLS Prototyping Polymer Unfilled White PA 11 that is formulated for easy processing across all LS platforms. Tightly controlled particle distribution creates a smooth surface finish and excellent feature detail. Parts prod.. |
|||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 2 in/min; ASTM D638 |
| A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||