Cossa Polimeri ESTABLEND 4500 V0 HF Flame Retardant PC - ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTABLEND
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTABLEND 4500 V0 HF Flame Retardant PC - ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC - ABS BlendFlame retardant class V0, chlorine and bromine free, good light resistance, excellent mechanical properties, excellent processabilityInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D 955
Melt Flow 30 g/10 min

@Load 5.00 kg,
Temperature 240 °C
30 g/10 min

@Load 11.0 lb,
Temperature 464 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
ASTM D 638
Tensile Strength, Yield 50.0 MPa
7250 psi
ASTM D 638
Elongation at Break 40 %
40 %
ASTM D 638
Flexural Modulus 2.60 GPa
377 ksi
ASTM D 790
Izod Impact, Notched 5.00 J/cm

@Temperature 0.000 °C
9.37 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
5.50 J/cm

@Temperature 23.0 °C
10.3 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 94.0 °C

@Load 5.00 kg
201 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
105 °C

@Load 0.999 kg
221 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Glow Wire Test 960 °C
1760 °F
I.E.C. 695-2-1