SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* KL003 is a compound based on Acetal Copolymer resin containing 15% PTFE. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.290 % | 0.290 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 16 % | 16 % | 5 mm/min; ISO 527 |
| 19 % | 19 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.0 % | 9.0 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.46 GPa | 357 ksi | 1 mm/min; ISO 527 |
| 2.53 GPa | 367 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 321 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.24 GPa | 325 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.10 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.17 | 0.17 | ASTM D3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm³/N-M | 11.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 107 µm/m-°C @Temperature -30.0 - 30.0 °C |
59.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 107 µm/m-°C @Temperature -30.0 - 30.0 °C |
59.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-JAC CJ-021 Flat Cable EMI Shield
- SABIC Innovative Plastics LNP STAT-KON WE003ER PBT (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
- EMS-Grivory Grivory® TSG-35/4 H black 9836 PA666-GF35
- Dow VORANOL™ CP 755 Polyol
- 3M FM152 Indoor UL Recognized Computer Imprintable Silver Polyester Label Product
- Solvay Specialty Polymers AvaSpire® AV-650 GF30 Polyaryletherketone (PAEK) (Unverified Data**)
- Teknor Apex Monprene® MP-2770 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved