SABIC Innovative Plastics NORYL PN275F PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PN275F PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS with low mineral loading. High heat, platable applications. NSF approved for water contact applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.3 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.3 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 34 % | 34 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.6 % | 6.6 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.13 GPa | 309 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 44.0 J @Temperature 23.0 °C |
32.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 151 °C | 304 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PH 69 GF 30 Polypropylene reinforced with glass fiber
- Polymax® Maxelast® C4960M TPE, Transparent
- Osprey Metals Fe3Si Binary Alloy Powder (Grade 90% - 16)
- Proto3000 Accura® Amethyst™ Material for use with Viper™ SLA® systems
- Nitriflex Nitrigum 25 FA Styrene Butadiene Rubber
- Overview of materials for Fluorinated Ethylene Propylene (FEP), Molded/Extruded
- Latrobe DuraTechâ„¢ Xtreme Powder Metal Tool Steel
- Saint-Gobain Fluoroloy® A12 High Performance Seal Material
- American Elements Silicon Nanoparticles
- Ensinger Tecatron® XP-65 Compression Molded PPS Compound, 30% Fiberglass with 15% PTFE
Copyright © lookpolymers.com All Rights Reserved