Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® DMX6014 PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DMX6014 is an injection moldable PC copolymer ABS blend. This resin combines excellent scratch resistance (F-pencil hardness) with ductility.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D 792
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 90
90
ASTM D 785
Hardness, Rockwell R 117
117
ASTM D 785
Tensile Strength at Break 45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D 638
48.0 MPa
6960 psi
50 mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D 638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Elongation at Break 45 %
45 %
Type I, 50 mm/min; ASTM D 638
50 %
50 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D 638
5.5 %
5.5 %
50 mm/min; ISO 527
Tensile Modulus 2.15 GPa
312 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 75.0 MPa
10900 psi
1.3 mm/min, 50 mm span; ASTM D 790
78.0 MPa
11300 psi
2 mm/min; ISO 178
Flexural Modulus 2.15 GPa
312 ksi
2 mm/min; ISO 178
2.20 GPa
319 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.700 J/cm

@Temperature -30.0 °C
 1.31 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
2.20 J/cm

@Temperature 23.0 °C
 4.12 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 55.0 J
40.6 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Hot Ball Pressure Test <= 100 °C
<= 212 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
113 °C

@Thickness 3.20 mm
 235 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
97.0 °C

@Thickness 3.20 mm
 207 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 113 °C
235 °F
Rate B/50; ASTM D 1525
113 °C
235 °F
Rate B/50; ISO 306
118 °C
244 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 2nd value; UL 94
Glow Wire Test 650 °C

@Thickness 1.50 mm
 1200 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
 2.8

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 IEC 60250
3.0

@Frequency 1000 Hz
 3.0

@Frequency 1000 Hz
 IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.60 mm
 889 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
47.0 kV/mm

@Thickness 0.800 mm
 1190 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
0.012

@Frequency 1000 Hz
 0.012

@Frequency 1000 Hz
 IEC 60250
0.030

@Frequency 50.0 - 60.0 Hz
 0.030

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C pass
IEC 60695-10-2
Erichson scratch depth, 6N, micrometer 14
SABIC Method
Pencil Hardness test, 1kgf F
ASTM D 3363