BLUESTAR LXS 109 PPE-PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Unreinforced |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR LXS 109 PPE-PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Electrical partsFire RatedInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 300 °C |
60 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | type I; ASTM D638 |
| Elongation at Break | 50 % | 50 % | type I; ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer (Asia Pacific)
- ACC QSil 551 QSI Quantum Silicones Silicone Potting Material (discontinued **)
- Materion Beryllium Copper Alloy 245CT Castings (UNS C82600)
- LG Chemical LUPOL TE-5104K Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Modulus
- Dow Corning Q1-2333 CHEMICAL GRADE TRICHLOROSILANE
- Colorite Polymers 9812-15 Radiopaque Vinyl Compound
- Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding
- E-Polymers EFLEX® V1060 EPDM/TPV
- BASF Neopolen® P 9270 0.11 g/cc Core density; Expanded Polypropylene (Europe)
- PolyOne Synprene® IT 39-020 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved