SABIC Innovative Plastics LNP Stat-kon TE002

Category Polymer , Thermoplastic , Polyurethane, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon TE002.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* TE002 is a compound based on Polyurethane resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D 792
1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.60 %
0.60 %
23°C / 50% RH; ISO 62
0.46 %

@Time 86400 sec
 0.46 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
Type I, 5 mm/min; ASTM D 638
49.0 MPa
7110 psi
5 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
5 mm/min; ISO 527
52.0 MPa
7540 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 19.8 %
19.8 %
5 mm/min; ISO 527
22.8 %
22.8 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 15.7 %
15.7 %
5 mm/min; ISO 527
19.2 %
19.2 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 1.30 GPa
189 ksi
50 mm/min; ASTM D 638
1.58 GPa
229 ksi
1 mm/min; ISO 527
Flexural Strength 51.0 MPa
7400 psi
ISO 178
Flexural Modulus 1.16 GPa
168 ksi
1.3 mm/min, 50 mm span; ASTM D 790
1.66 GPa
241 ksi
2 mm/min; ISO 178
Izod Impact, Notched 4.78 J/cm

@Temperature 23.0 °C
 8.95 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 16.89 J/cm

@Temperature 23.0 °C
 31.64 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 37.0 kJ/m²

@Temperature 23.0 °C
 17.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 128 kJ/m²

@Temperature 23.0 °C
 60.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 15.0 J
11.1 ft-lb
Multiaxial Impact; ISO 6603
23.0 J

@Temperature 23.0 °C
 17.0 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 1.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 0.556 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 16.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 8.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
 286 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
82.0 °C

@Thickness 3.20 mm
 180 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 5.0 - 8.0 ohm
5.0 - 8.0 ohm
ASTM D 257