A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | POLYPUR™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
48 hr, at 80 and 121°C; ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
72 hr; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | 15 sec delay; ASTM D2240 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 30 % | 30 % | 2 in/min; ASTM D412 |
| Flexural Modulus | 1.725 GPa | 250.2 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.65 J/cm | 10.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Momentive Performance Materials RTV5222 Neutral Cure, One Component RTV Adhesive Sealant
- Lavergne VYTEEN ABS 2904 Acrylonitrile Butadiene Styrene
- SGL Carbon Group PANOX® SA C063 EEA High performance oxidized textile fiber, Crimped staple fiber, For carbon/carbon and spinning
- Shin-Etsu Silicones KF-9008 Fluid
- Samsung Cheil Industries Infino® GP-5400G PBT, 40% Glass Filled
- Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Conditioned (2.5% Moisture)
- Bhansali Engineering Abstron SE-22 ABS Sheet Extrusion Grade
- LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement (discontinued **)