SABIC Innovative Plastics LNP LUBRICOMP GX07409H PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP GX07409H PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* GX07409H is a compound based on PSU resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0051 - 0.0071 cm/cm @Time 86400 sec |
0.0051 - 0.0071 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0063 - 0.0083 cm/cm @Time 86400 sec |
0.0063 - 0.0083 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 9.3 % | 9.3 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 5.8 % | 5.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.52 GPa | 365 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.64 GPa | 383 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 219 kJ/m² | 104 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 167 °C | 333 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Nye Lubricants 392 (RL) Synthetic Oil
- Precision Polymer Engineering S65T Silicone Rubber
- Inno-Comp INNOPOL® CS 2-3130 NU UV-Stabilized 30% Talc-Filled Polypropylene Block-Copolymer
- Kraton® G1654 H (SEBS) Linear Triblock Copolymer
- Samyang Tribit® 1503S Polybutylene Terephthalate
- Eagle Brass 425 Tin Brass 2%, 3/4 Hard
- Ensinger Tecapeek® XP-98 Compression Molded PEEK Compound, 30% Carbon Fiber
- ExxonMobil 22 Mobil EAL Arctic Series
- DuPont Teijin Films Melinex® 473 Polyester Film, 200 Gauge
Copyright © lookpolymers.com All Rights Reserved