- SABIC Innovative Plastics Valox® 357U PBT+PC
SABIC Innovative Plastics Valox® 357U PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 357U PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced PC/PBT, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm @Thickness 0.750 - 2.30 mm |
0.0080 - 0.011 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.010 - 0.014 cm/cm @Thickness 2.30 - 4.60 mm |
0.010 - 0.014 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.013 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| Gardner Impact | 43.0 J | 31.7 ft-lb | ASTM D3029 |
| 43.0 J | 31.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 124 µm/m-°C @Temperature 60.0 - 138 °C |
68.9 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.460 mm |
HB @Thickness 0.0181 in |
UL 94 |
| V-0 @Thickness 0.640 mm |
V-0 @Thickness 0.0252 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 30 % | 30 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.20e+16 ohm-cm | >= 1.20e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
ASTM D150 |
| 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 18.5 kV/mm @Thickness 3.20 mm |
470 kV/in @Thickness 0.126 in |
in air; ASTM D149 |
| 18.5 kV/mm @Thickness 3.20 mm |
470 kV/in @Thickness 0.126 in |
in oil; ASTM D149 | |
| 25.2 kV/mm @Thickness 1.60 mm |
640 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
ASTM D150 |
| 0.030 @Frequency 1.00e+6 Hz |
0.030 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.75cm^3/g | ASTM D792 |
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200H-30 Fiberglass Reinforced Thermoset SMC
- Samsung Cheil Industries Starex® WR-9130 ASA, Unreinforced
- Solvay DURAPHOS® AP-240L Surfactant
- Zhejiang Juner 301-G20 20% Glass Fibre Reinforced and Flammable Resistant
- Eagle Brass 110 EPT COPPER, 1/2 Hard
- Dow Corning BF 20 PLUS ANTIFOAM EMULSION
- Esstech X-950-0000 BisGMA Resin, C29H36O8
- Eurotec® Tecomid® NB40 NL XA 20 PA 6 unreinforced, UL94 V0
- Wanhua Chemical Wanthane® WHT-1595 Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved