Polymer Property : Tensile Strength at Break = 14200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	98.0 MPa	14200 psi	50 mm/min; ASTM D638
Ovation Polymers RIGITRON 30525 GF FR PET, 25% Glass Reinforced PET – 25% Short Glass Fiber Reinforced with Flame retardant. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to AS..
Tensile Strength at Break	98.0 MPa	14200 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL349EF PC LNP LUBRICOMP* DFL349EF is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFP36 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFP36 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone.
Tensile Strength at Break	98.0 MPa	14200 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Tensile Strength at Break	98.0 MPa	14200 psi	ASTM D638
LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin..
Tensile Strength at Break	98.1 MPa @Thickness 3.20 mm	14200 psi @Thickness 0.126 in	50mm/min; ASTM D638
LG Chemical LupoxÂ® NH2306F PBT+GF30% Description: Injection Molding, PBT+GF30%, Halogen Free Flame RetardantApplication: IT/OA, E&E (Connector)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical
Tensile Strength at Break	98.0 MPa	14200 psi	ASTM D638
Kotec Carbotex KGN-15MRA Polycarbonate, Flame Retardant, 15% Glass Fiber Reinforced Features: Glass fiber 15% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod..
Tensile Strength at Break	98.0 MPa	14200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
Tensile Strength at Break	98.0 MPa	14200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE LNP* THERMOCOMP* 2X98703 is a compound based on ETFE Copolymer resin containint Proprietary Filler(s).
Tensile Strength at Break	98.1 MPa	14200 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength at Break	98.1 MPa	14200 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VG-4920F ABS, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength at Break	98.1 MPa	14200 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® HN-3203G PC, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength at Break	98.1 MPa	14200 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength at Break	98.0 MPa	14200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66 LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp ZF008 PPO LNP* Thermocomp* ZF008 is a compound based on Modified PPO containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod..
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	98.0 MPa	14200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66 LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant.
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus ..
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Asia Pacific) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus ..
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus ..
Tensile Strength at Break	98.0 MPa	14200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod..
Tensile Strength at Break	97.9 MPa	14200 psi	ASTM D638
PlastxWorld CEVIAN® S1230 PC/ABS alloy Glass fiber reinforced PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Tensile Strength at Break	98.0 MPa	14200 psi	DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-324V11T A3L PEEK Polymer, Reinforced Main Charactistics: Stress resistant; High impact strength at 196 ° C Applications: Shipbuilding; Chemical Engineering; Automitve Technology; Machine ToolsInformation provided by Zedex
Tensile Strength at Break	98.0 MPa	14200 psi	ISO 527
Azoty Tarnow™ TARNOFORM 300 GF4 POM 20% glass fiber reinforced injection molding grade with very high strength.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Tensile Strength at Break	98.2 MPa	14200 psi	ASTM D3759
3M 850 Polyester Film Tape 3M™ Polyester Film Tape 850 can generally be used for splicing and applications where chemical resistance and/or clean removal is necessary. The silver backing is a transparent polyester with a thi..
Tensile Strength at Break	98.0 MPa	14200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® K4530 PBT 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
Tensile Strength at Break	98.0 MPa	14200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004L PES LNP* THERMOCOMP* JF004L is a compound is based on Polyethersulfone containing 20% Glass Fiber. Characteristics of this grade is: Low Extractible
Tensile Strength at Break	97.9 MPa	14200 psi	ASTM D638
PlastxWorld CEVIAN® S5220 20% GF PC/ABS alloy Glass fiber reinforced and flame retarded PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld ..