- ETFE/ECTFE
- SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE
SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 2X98703 is a compound based on ETFE Copolymer resin containint Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | ASTM D792 |
| Density | 1.73 g/cc | 0.0625 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 |
| 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 101 MPa | 14600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 5.5 % | 5.5 % | 5 mm/min; ISO 527 |
| 5.9 % | 5.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.6 % | 5.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.22 GPa | 1627 ksi | 1 mm/min; ISO 527 |
| 14.18 GPa | 2057 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
| 143 MPa | 20700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 10.44 GPa | 1514 ksi | 2 mm/min; ISO 178 |
| 10.6 GPa | 1540 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 4.11 J/cm | 7.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.81 J/cm | 9.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 88.0 kJ/m² | 41.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 20.0 J @Temperature 23.0 °C |
14.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.44 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 239 °C | 462 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ HC 2175 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nilit FRIANYL A63 H-GV25 Nylon 6.6 for injection molding, 25% glass fiber reinforced
- DSM Somos® 7120 Epoxy Photopolymer, UV Postcure (discontinued **)
- PolyOne Therma-Tech™ SF-5000C TC Polyphenylene Sulfide (PPS) (discontinued **)
- Gouda Vuurvast AK 55 S Dense Refractory Brick
- Sekisui PIOCELAN LSP-20D Moldable Polymer Foam
- Lubrizol ESTANE® 5708F4 Ester Based Thermoplastic Polyurethane (European Grade)
- Chevron Phillips Marlex® H516HP High Density Polyethylene, Pressure Pipe Grade
- ConocoPhillips Hydroclear® 100 Turbine Oil
- ConocoPhillips SUPER-STA M NLGI No.1
Copyright © lookpolymers.com All Rights Reserved