SABIC Innovative Plastics LNP Thermocomp ZF008 PPO
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp ZF008 PPO.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* ZF008 is a compound based on Modified PPO containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D 792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D 638 |
| 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D 638 |
| 1.5 % | 1.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.70 GPa | 1410 ksi | 1 mm/min; ISO 527 |
| 10.46 GPa | 1517 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 144 MPa | 20900 psi | ISO 178 |
| 149 MPa | 21600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 9.55 GPa | 1390 ksi | 2 mm/min; ISO 178 |
| 9.91 GPa | 1440 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.960 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.28 J/cm @Temperature 23.0 °C |
8.02 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 46.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPC-20G Black Polypropylene Copolymer (PP Copolymer)
- Nye Lubricants UniFlor 8622 (851) (UF) Synthetic Oil
- Nylacast Nylube MO Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant), MoS2 Filled
- S&E Specialty Polymers TufTech™ GA-1038 Natural MA PVC Compound
- SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
- Stir SpA SA 68 R (PVC)
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- Covestro Bayblend® FR3012 PC/ABS Blend
- Chosun Refractories CFA-2 Ceramic Foam
- BASF Capron® 8351 Impact Modified Nylon 6 (Conditioned) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved