Samsung Cheil Industries Infino® HN-3203G PC, Glass Filled FR
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HN-3203G PC, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Temperature 23.0 °C |
0.15 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 250 °C |
11 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 4.1 % | 4.1 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.81 GPa | 697 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 157 MPa | 22800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 5.39 GPa | 782 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.57 J/cm @Thickness 3.17 mm |
2.94 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C @Thickness 6.40 mm |
293 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 147 °C | 297 °F | B/50; ISO R306 |
| 150 °C | 302 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 - 6.00 mm |
V-0 @Thickness 0.0591 - 0.236 in |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CH120 Polypropylene, Homopolymer, Injection Molding, Barefoot
- Honeywell Aegis™ HCA95QP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- IDI Composites E-203 Thermoset Polyester, Sheet
- Materion Beryllium Copper Alloy 10 Wire; HT (TH04) Temper; 1.3-12.7 mm Diameter (UNS C17500)
- SSAB Tunnplat Domex® 550MC HSLA Steel
- SABIC Innovative Plastics LNP THERMOCOMP EXTC8141 PC (Asia Pacific)
- Wellman Wellamid® GSF1849-N1 Nylon 66, 40% Glass Sphere/Fiber Reinforced
- Zotefoams Plastazote® MP15FR Metallocene Polyethylene Foam, Flame Retardant
- DuPont Teijin Films Mylar® MLB Polyester Film, 48 Gauge
Copyright © lookpolymers.com All Rights Reserved