Azoty Tarnow™ TARNOFORM 300 GF4 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 GF4 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass fiber reinforced injection molding grade with very high strength.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0245 cm/cm @Thickness 4.00 mm |
0.0245 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0265 cm/cm | 0.0265 in/in | 60x60x4; ISO 294-4 |
| Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.0 MPa | 14200 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.21 J/g-°C | 0.289 BTU/lb-°F | |
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75 |
| Vicat Softening Point | 163 °C | 325 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Dissipation Factor | 0.0095 @Frequency 1e+6 Hz |
0.0095 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | Barrel temperature |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
Users viewing this material also viewed the following:
- Oceanchem Group Calcium Chloride 74-77% flakes
- LyondellBasell Lupolen® 3652 D SW 00413 MDPE
- Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
- Saint-Gobain Meldin® 7022 CM Compression Molded Graphite Filled Polyimide
- Sumitomo Bakelite Durez® 32245 Phenolic, Compression Grade
- TIMET TIMETAL® 15-3 Titanium Alloy (Ti-15V-3Cr-3Sn-3Al); Aged at 538°C
- Dow DOWLEX™ 2244A Linear Low Density Polyethylene, Cast Film Grade
- Dow SPECTRIM™ 50-S Reaction Moldable Polymer
- Colorite Polymers 8534 General Purpose Vinyl Compound
- Asahi Kasei Xyron® X0700 Modified Polyphenylene Ether
Copyright © lookpolymers.com All Rights Reserved