SABIC Innovative Plastics ValoxÂ® K4530 PBT (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Valox®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics ValoxÂ® K4530 PBT (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.

Physical Properties	Metric	English	Comments
Specific Gravity	1.41 g/cc	1.41 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Thickness 3.20 mm	0.0070 - 0.0090 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.010 - 0.012 cm/cm @Thickness 3.20 mm	0.010 - 0.012 in/in @Thickness 0.126 in	SABIC Method
Melt Index of Compound	17 g/10 min @Load 2.16 kg, Temperature 250 Â°C	17 g/10 min @Load 4.76 lb, Temperature 482 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D638
	89.0 MPa	12900 psi	Type I, 5 mm/min; ASTM D638
	98.0 MPa	14200 psi	Type I, 5 mm/min; ASTM D638
	98.0 MPa	14200 psi	5 mm/min; ISO 527
	103 MPa	14900 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	98.0 MPa	14200 psi	5 mm/min; ISO 527
	103 MPa	14900 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	2.3 %	2.3 %	Type I, 5 mm/min; ASTM D638
	2.5 %	2.5 %	Type I, 5 mm/min; ASTM D638
	3.1 %	3.1 %	5 mm/min; ISO 527
	3.8 %	3.8 %	Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
	4.0 %	4.0 %	Type I, 5 mm/min; ASTM D638
	4.0 %	4.0 %	Type I, 5 mm/min; ASTM D638
	6.0 %	6.0 %	Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
	7.0 %	7.0 %	Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
	9.7 %	9.7 %	Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
Elongation at Yield	3.1 %	3.1 %	5 mm/min; ISO 527
	4.0 %	4.0 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	3.55 GPa	515 ksi	5 mm/min; ASTM D638
	5.25 GPa	761 ksi	1 mm/min; ISO 527
Flexural Strength	150 MPa	21800 psi	1.3 mm/min, 50 mm span; ASTM D790
	150 MPa	21800 psi	2 mm/min; ISO 178
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
Flexural Modulus	4.52 GPa	656 ksi	1.3 mm/min, 50 mm span; ASTM D790
	4.64 GPa	673 ksi	1.3 mm/min, 50 mm span; ASTM D790
	4.75 GPa	689 ksi	2 mm/min; ISO 178
	4.82 GPa	699 ksi	1.3 mm/min, 50 mm span; ASTM D790
	5.10 GPa	740 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.580 J/cm	1.09 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.00 J/cm	7.49 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	30.0 kJ/mÂ²	14.3 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	4.00 J	2.95 ft-lb	ASTM D3763
	5.00 J	3.69 ft-lb	ASTM D3763
	6.00 J	4.43 ft-lb	ASTM D3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	218 Â°C @Thickness 3.20 mm	424 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	193 Â°C @Thickness 3.20 mm	379 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	205 Â°C	401 Â°F	Rate B/120; ISO 306