LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic

Category Polymer , Thermoplastic
Manufacturer LG Chemical
Trade Name LUCON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solving problems associated with build-up of electrostatic charges, electrostatic discharge, and electromagnetic interference. These materials span the surface resistivity spectrum from antistatic through conductive to EMI shielding (100-1012O).Applications: I.C. tray, wafer carrier, I.C. magazine, notebook PC case, home appliance part, LCD cassette trayInformation Provided by LG Chem
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80
80
ASTM D785
Tensile Strength at Break 98.0 MPa
14200 psi
ASTM D638
Elongation at Break <= 10 %
<= 10 %
ASTM D638
Flexural Strength 137 MPa
19900 psi
ASTM D790
Flexural Modulus 8.83 GPa
1280 ksi
ASTM D790
Izod Impact, Notched 0.490 J/cm
0.918 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity >= 0.250 W/m-K
>= 1.74 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1e+05 - 1.00e+6 ohm-cm
1e+05 - 1.00e+6 ohm-cm
ASTM D257
Surface Resistance 1e+05 - 1.00e+6 ohm
1e+05 - 1.00e+6 ohm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 300 - 350 °C
572 - 662 °F
Middle Barrel Temperature 300 - 350 °C
572 - 662 °F
Front Barrel Temperature 300 - 350 °C
572 - 662 °F
Nozzle Temperature 300 - 350 °C
572 - 662 °F
Melt Temperature 310 - 360 °C
590 - 680 °F
Mold Temperature 80.0 - 150 °C
176 - 302 °F
Drying Temperature 110 - 120 °C
230 - 248 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 49.03 - 78.45 MPa
7111 - 11380 psi
Second
58.8 - 118 MPa
8530 - 17100 psi
First
Back Pressure 0.000 - 3.92 MPa
0.000 - 569 psi
Screw Speed 40 - 80 rpm
40 - 80 rpm