SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required.Thermocomp ZX09022 is an opaque material available in limited colors only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| 101 MPa | 14600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| 101 MPa | 14600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| 101 % | 101 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.60 GPa | 1100 ksi | 5 mm/min; ASTM D638 |
| 7.70 GPa | 1120 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 141 MPa | 20500 psi | 2 mm/min; ISO 178 |
| 144 MPa | 20900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.10 GPa | 1030 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.950 J/cm | 1.78 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.50 J/cm | 12.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| 42.0 kJ/m² @Temperature -30.0 °C |
20.0 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.90 J/cm² | 18.6 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.60 J/cm² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Dart Drop, Total Energy | 10.0 J @Temperature -30.0 °C |
7.38 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 25.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
13.9 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature -30.0 - 80.0 °C |
66.7 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| 130 µm/m-°C @Temperature -40.0 - 95.0 °C |
72.2 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 166 °C @Thickness 3.20 mm |
331 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 150 °C | 302 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
UL 94 |
| Glow Wire Test | 650 °C @Thickness 3.00 mm |
1200 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Rotuba 870 Ethyl Cellulose
- Total Lacqtene® 2006 TN 35 HDPE pipe coating (discontinued **)
- Lubriplate HO Special Hydraulic Oil Specialty Oil and Fluid
- Fainplast Compounds GS 90/T Flexible PVC, Injection Molding for Footwear
- Dow Corning 1785 EMULSION
- 3M 7850TL Laser Toner Printable Polyester Label Material
- Beijing Evergrow Resources CFC-DDX-1000 Carbon Fiber Cloth
- Lubrizol Estane® 58252 Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved