Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 80.0 MPa | 11600 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PH 69 GF 30 Polypropylene reinforced with glass fiber Modified homopolymer PP for injection molding, reinforced with 30% glass fiber. Applied in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Pl.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 6 G 5 Polyamide 6, 5% Graphite FeaturesPA 6 for injection moulding with addition of 5% graphite, the PA surface rolling resistance force is significantly lowered. Used mainly in the product of crates and cases for bearings, slid.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
Nilit FRIANYL B63 W-KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® DP 1852/30 000000 Nylon 6, 30% Glass Fiber PA 6, 30% glassfibers, UL V-0 at 0.75 mm (listed),GWIT:775°C at 0,75 mm, GWFI:960°C at 0.75 mm, CTI/A:400, good flowabilityApplication Examples: Hand-held barrel pump housings |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
Grupo Repol Dinalon® B3S25 PA6 Unreinforced Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | |
LATI Latiohm 80-05 CNT GCE/500 PPS, Glass/Mineral Reinforced Semiconductive/dissipative product based on Polyphenylene Sulfide (PPS). Carbon nanotubes. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem 1110V PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 4002 PEI PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 |
Sumitomo Bakelite North America Epiall® 1908-1 Short Glass Fiber Reinforced Epoxy Epiall 1908-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation proper-ties that meets the requir.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN2V PPE+HIPS (Europe-Africa-Middle East) NORYL GFN2V is a 20 % glass fibre reinforced material with a HDT/A of 130C according ISO 75. NORYL GFN2V cust spec 1977 has been approved for potable water applications up to 85C by the UK WFBS acco.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 1110 PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem 1110V PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-93 |
Wellman Wellamid® 22LH-NBK4 Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-93 |
Wellman Wellamid® NY1599-BK11 Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | |
Toyobo ECOVYLOPET® EMC2311 PET Bottle Recycling Grade, 10% Glass Reinforced Features: PET Bottle Recycling Grade, 10% Glass Fiber Reinforced, General PurposeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled PP homopolymer 30% chemically coupled glass fiber reinforcedHigh melt flow rate, excellent impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6600 GV 15 HWCP 15% Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-15H nat PA12-GF15 Product description: Grilamid LV-15H is a 15% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following product profile: very low water absorptiongood dimension.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
Eurotec® Tecomid® NA40 NL XA 20 PA 6.6 unreinforced, UL94 V0 Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 [mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® A3 GF 15 (2418) PA 6.6 Conditioned, 15% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Tensile Strength at Break | 80.0 MPa @Temperature -40.0 °C |
11600 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8202 PA6 (Conditioned) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | MD |
BASF Ultramid® C33 LN 0.025 mm Blown Film PA6/66 Description: Ultramid® C33 LN is a copolyamide 6/66 grade of intermediate viscosity for the production of mulitlayer film. Its lower melting point than standard PA 6 is advantageous for coextrusion.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | Conditioned; ISO R 527 |
Addiplast Addinyl B2I V25 Flame Retardant Nylon 6, 25% Glass Filled Flame retardant, 25% glass fiber reinforced, halogen freeInformation provided by Addiplast. |
|||
Tensile Strength at Break | 80.0 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec |
11600 psi @Temperature 266 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Dry, 20% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Tensile Strength at Break | 80.0 MPa | 11600 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® C33 01 PA66/6 (Dry) Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to F.. |