A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer A. Schulman, Inc.
Trade Name SCHULAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.014 cm/cm

@Thickness 3.175 mm
 0.0040 - 0.014 in/in

@Thickness 0.1250 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
ASTM D638
Tensile Modulus 4.299 GPa
623.5 ksi
ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 295 - 305 °C
563 - 581 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying