Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 30% chemically coupled glass fiber reinforcedHigh melt flow rate, excellent impact strengthInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D 955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 6.60 GPa | 957 ksi | ASTM D 638 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature -20.0 °C |
1.50 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.900 J/cm @Temperature 0.000 °C |
1.69 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 1.00 J/cm @Temperature 23.0 °C |
1.87 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 130 °C @Load 5.00 kg |
266 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® VR2520 PC
- Garlock GYLON® 3565 ENVELON® PTFE Gasketing, Glass Microsphere Filled
- Latrobe Starkâ„¢ ASTM M4 High Speed Steel
- Kuraray SEPTON® A3 Hot Melt Adhesive
- Solvay TECHNYL® A 218G1 V30 Black 34N PA66, 30% glass fiber, DRY
- SABIC Innovative Plastics NORYL WCP921A PPE-TPE (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer
- Zotefoams Plastazote® LD15FMSV Low Density Polyethylene Foam, Flame Retarded
- PolyOne Synprene® RT-3615 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved