LATI Latiohm 80-05 CNT GCE/500 PPS, Glass/Mineral Reinforced

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer	LATI
Trade Name	Latiohm
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 80-05 CNT GCE/500 PPS, Glass/Mineral Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polyphenylene Sulfide (PPS). Carbon nanotubes. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.812 g/cc	0.06546 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0030 - 0.0040 cm/cm	0.0030 - 0.0040 in/in
Linear Mold Shrinkage, Transverse	0.0070 - 0.010 cm/cm	0.0070 - 0.010 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	80.0 MPa	11600 psi
Elongation at Break	0.50 %	0.50 %
Tensile Modulus	15.7 GPa	2280 ksi
Charpy Impact Unnotched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²
Charpy Impact, Notched	0.300 J/cmÂ²	1.43 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	280 Â°C	536 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	270 Â°C	518 Â°F
Vicat Softening Point	255 Â°C @Load 5.00 kg	491 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	10000 ohm-cm	10000 ohm-cm
Surface Resistance	3000 ohm	3000 ohm

Processing Properties	Metric	English
Melt Temperature	290 - 310 Â°C	554 - 590 Â°F
Mold Temperature	120 - 130 Â°C	248 - 266 Â°F
Drying Temperature	130 - 150 Â°C @Time 10800 sec	266 - 302 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa