SABIC Innovative Plastics ULTEM 4002 PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 4002 PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors.
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Moisture Absorption 0.600 %
0.600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.1 %
1.1 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 9.5 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 9.5 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 13 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
50 mm/min; ISO 527
85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 100 MPa
14500 psi
50 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 25 %
25 %
50 mm/min; ISO 527
40 %
40 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 5 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 3.30 GPa
479 ksi
1 mm/min; ISO 527
3.46 GPa
502 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 130 MPa
18900 psi
2 mm/min; ISO 178
155 MPa
22500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
3.55 GPa
515 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.17 J/cm
2.19 ft-lb/in
ASTM D256
1.20 J/cm

@Temperature -30.0 °C
 2.25 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 380 J

@Temperature 23.0 °C
 280 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 39.0 µm/m-°C

@Temperature -40.0 - 150 °C
 21.7 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
39.0 µm/m-°C

@Temperature 23.0 - 150 °C
 21.7 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature -40.0 - 150 °C
 22.2 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
40.0 µm/m-°C

@Temperature 23.0 - 150 °C
 22.2 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
197 °C

@Thickness 3.20 mm
 387 °F

@Thickness 0.126 in
 unannealed; ASTM D648
200 °C

@Thickness 6.40 mm
 392 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 210 °C
410 °F
Rate B/120; ISO 306
215 °C
419 °F
Rate B/50; ISO 306
219 °C
426 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 UL 94
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2