Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ASTM D792
1.33 g/cc
0.0480 lb/in³
ISO 1183
Moisture Absorption 0.0900 %
0.0900 %
50% RH, 24 hrs; ASTM D570
0.140 %
0.140 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5 mm/min; ISO 527
83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 80.0 MPa
11600 psi
5 mm/min; ISO 527
83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.6 %
2.6 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.6 %
2.6 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.88 GPa
708 ksi
1 mm/min; ISO 527
5.12 GPa
743 ksi
50 mm/min; ASTM D638
Flexural Strength 115 MPa
16700 psi
ISO 178
123 MPa
17800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 127 MPa
18400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.48 GPa
650 ksi
2 mm/min; ISO 178
4.60 GPa
667 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.780 J/cm
1.46 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.22 J/cm
9.78 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 31.0 kJ/m²
14.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 16.0 J

@Temperature 23.0 °C
 11.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 41.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 22.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 35.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
 286 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
115 °C

@Thickness 3.20 mm
 239 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Users viewing this material also viewed the following: