Lanxess Durethan® DP 1852/30 000000 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 1852/30 000000 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glassfibers, UL V-0 at 0.75 mm (listed),GWIT:775°C at 0,75 mm, GWFI:960°C at 0.75 mm, CTI/A:400, good flowabilityApplication Examples: Hand-held barrel pump housings
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.669 g/cc | 0.06030 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 134 cm³/g | 134 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0023 cm/cm | 0.0023 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0055 cm/cm | 0.0055 in/in | ISO 294-4, 2577 |
| Melt Flow | 55 g/10 min @Load 5.00 kg, Temperature 260 °C |
55 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Conditioned; ISO 527-1/-2 |
| 140 MPa | 20300 psi | ISO 527-1/-2 | |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | Conditioned; ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| 3.4 % | 3.4 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 3.0 % | 3.0 % | Conditioned; ISO 527-1/-2 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | Conditioned; ISO 527-1/-2 |
| 11.0 GPa | 1600 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 34.5 kV/mm | 876 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Lubricants | ||
| Release agent | ||
| Features | Flame retardant | |
| U.V. stabilized or stable to weather | ||
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MF,14,-110, GF30; ISO 1043-PA GF FR(17+72) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Network Polymers Nylon 0304NL
- Pyrotek Pyrethrum FA 800 Woven Stainless Steel Fabric
- Honeywell Aegis™ OX High Barrier Nylon (discontinued **)
- Hybrid Plastics POSS® MA0711 MethacrylDisilanolCyclopentyl-POSS®
- Lanxess Durethan® DP AKV 30 X HR EF 900116 Nylon 66, 30% Glass Fiber
- Lucas-Milhaupt Silvaloy® 5 Brazing Alloy
- A. Schulman POLYBATCH™ Green 3011E Concentrate Based In Polyethylene
- Trelleborg S561 Silicone Rubber
- Dow C702-20 Polypropylene Impact Copolymer
- Bisalloy Steels BisPlate 400 Thickness 16-80 mm
Copyright © lookpolymers.com All Rights Reserved