SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.

Physical Properties	Metric	English	Comments
Density	1.52 g/cc	0.0549 lb/inÂ³	ASTM D 792
	1.52 g/cc	0.0549 lb/inÂ³	ISO 1183
Moisture Absorption at Equilibrium	0.20 % @Time 86400 sec	0.20 % @Time 24.0 hour	50% RH; ASTM D 570
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Time 86400 sec	0.011 - 0.013 in/in @Time 24.0 hour	ASTM D 955
	0.012 cm/cm @Time 86400 sec	0.012 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
	0.020 cm/cm @Time 86400 sec	0.020 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	79.0 MPa	11500 psi	ISO 527
	80.0 MPa	11600 psi	ASTM D 638
Tensile Strength, Yield	80.0 MPa	11600 psi	ASTM D 638
	80.0 MPa	11600 psi	ISO 527
Elongation at Break	1.9 %	1.9 %	ISO 527
	2.1 %	2.1 %	ASTM D 638
Elongation at Yield	1.9 %	1.9 %	ISO 527
	2.1 %	2.1 %	ASTM D 638
Tensile Modulus	7.14 GPa	1040 ksi	1 mm/min; ISO 527
	7.58 GPa	1100 ksi	50 mm/min; ASTM D 638
Flexural Strength	115 MPa	16700 psi	ISO 178
	117 MPa	17000 psi	ASTM D 790
Flexural Modulus	6.00 GPa	870 ksi	ISO 178
	6.20 GPa	899 ksi	ASTM D 790
Izod Impact, Notched	0.530 J/cm @Temperature 23.0 Â°C	0.993 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Unnotched	4.48 J/cm @Temperature 23.0 Â°C	8.39 ft-lb/in @Temperature 73.4 Â°F	ASTM D 4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ² @Temperature 23.0 Â°C	2.38 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	27.0 kJ/mÂ² @Temperature 23.0 Â°C	12.8 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U
Impact Test	2.00 J	1.48 ft-lb	Multiaxial Impact; ISO 6603
	9.00 J @Temperature 23.0 Â°C	6.64 ft-lb @Temperature 73.4 Â°F	Instrumented Impact Energy @ peak; ASTM D 3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	10.8 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	6.00 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	113 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	62.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	3.60 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	2.00 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	44.3 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	24.6 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	165 Â°C	329 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	162 Â°C @Thickness 3.20 mm	324 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	157 Â°C	315 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	160 Â°C @Thickness 3.20 mm	320 Â°F @Thickness 0.126 in	unannealed; ASTM D 648

Users viewing this material also viewed the following: