SABIC Innovative Plastics Ultem 1110V PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem 1110V PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D 792 |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.65 % | 0.65 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.2 % @Temperature 23.0 °C |
1.2 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| 21 g/10 min @Load 5.00 kg, Temperature 360 °C |
21 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
| 110 MPa | 16000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 60 % | 60 % | 5 mm/min; ISO 527 |
| 70 % | 70 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| 3.72 GPa | 540 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.72 GPa | 540 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.560 J/cm @Temperature 23.0 °C |
1.05 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.560 J/cm @Temperature -30.0 °C |
1.05 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 21.0 J/cm @Temperature 23.0 °C |
39.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 28.0 J @Temperature 23.0 °C |
20.7 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 197 °C @Thickness 3.20 mm |
387 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 199 °C @Thickness 6.40 mm |
390 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/50; ISO 306 |
| 205 °C | 401 °F | Rate B/120; ISO 306 | |
| 219 °C | 426 °F | Rate B/50; ASTM D 1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Flammability, UL94 | V-1 @Thickness 0.750 mm |
V-1 @Thickness 0.0295 in |
UL 94 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 50.0 - 60.0 Hz |
3.5 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| Dielectric Strength | 17.2 kV/mm @Thickness 3.20 mm |
437 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0016 @Frequency 50.0 - 60.0 Hz |
0.0016 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| Comparative Tracking Index | >= 125 V | >= 125 V | IEC 60112 |
| 175 V | 175 V | IEC 60112 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Asia Pacific)
- Kraton® D1163 P (SIS) Linear Triblock Copolymer
- SABIC Innovative Plastics ULTEM PW1000 PEI (Europe-Africa-Middle East)
- Spartech Royalite R922 PC/ABS Aircraft Grade Sheet
- Techmer ES HiFill® PA6 GF33 UG HS BK 33% Glass Filled
- A. Schulman POLYBATCH™ Yellow LL20203/2 Concentrate Based In LDPE
- Elastomer Engineering E57L Polyurethane
- 3M 9088 High Performance Double Coated Tapes with Adhesive 375
- Austin Novel Materials Texalan® 798A PCL TPU
Copyright © lookpolymers.com All Rights Reserved