- Polymer Property : Tensile Strength at Break = 127 MPa
Polymer Property : Tensile Strength at Break = 127 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 127 MPa | <= 18400 psi | ISO/R527 |
| Polykemi AB SCANMID 6 B12^ F30 AS Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| Nilit FRIANYL B63 FK 2010 Nylon 6 for injection molding, 20% glass fiber and 10% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 127 MPa @Thickness 3.20 mm |
18400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical Lupox® GP2306FC PBT+GF30% Description: Injection Molding, PBT+GF30%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical |
|||
| Tensile Strength at Break | 127 MPa @Thickness 3.20 mm |
18400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical Lupox® GP2306FS PBT+GF30% Description: Injection Molding, PBT+GF30%, Flame Retardant, Anti-Hydrolysis Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chem.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| Kotec Carbotex KG-30MRA Polycarbonate, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| Kotec Carbotex KGN-30MRA Polycarbonate, Flame Retardant, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12 LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6 (Asia Pacific) LNP* Lubricomp* PFL34 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the As.. |
|||
| Tensile Strength at Break | 127 MPa @Temperature 100 °C |
18400 psi @Temperature 212 °F |
ISO 527-2 |
| Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) Amodel® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifica.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific) 40% GR, increased strength/stiffness vs unreinforced. Non-flame retardant. For appliance handles, spotlights, electric motors, pump housings etc.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear LNP* STAT-KON* OCL32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66 LNP* STAT-KON* RE004MPC is a compound based on Nylon 66 resin containing 20% Milled Carbon Fiber. Added features of this material are: Exceptional Processing, Clean Compound System, Electrically C.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON WE003ER PBT (Europe-Africa-Middle East) LNP* Stat-kon* WE003ER is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Easy Molding, Easy Release, Electrically Conductive. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0069P PC LNP THERMOCOMP* DF0069P is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008SU PP LNP VERTON* MV008SU is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008SU PP (Asia Pacific) LNP VERTON* MV008SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP XFL36 AMORPHOUS POLYAMIDE LNP* LUBRICOMP* XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_HM4025 compound is a 40% Glass/Mineral filled high modulus grade. DTUL 255F (124C). UL94 V-0/V-1/5VA rated in black and gray only (see thicknesses). |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008SXP PP (Europe-Africa-Middle East) LNP* Verton* MV008SXP is a compound based on Polypropylene resin containing Long Glass. Added features include: Chemically Coupled, Heat Stabilized. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 127 MPa @Temperature 100 °C |
18400 psi @Temperature 212 °F |
ISO 527-2 |
| Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically .. |
|||