- A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT
A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | VOLOY™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.175 mm |
0.0030 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 182 MPa | 26400 psi | ASTM D790 |
| Flexural Modulus | 10.2 GPa | 1480 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.06 J/cm | 7.60 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GPP1001HFNH-2-AT(18) PP
- Nitriflex NP-2150 Powdered Nitrile
- Nilit FRIANYL A63 KV40 Nylon 6.6 for injection molding, 40% glass ball reinforced
- Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact
- A. Schulman POLYFORT™ FPP 1605 Glass Reinforced Chemically Coupled Copolymer
- American Elements Hafnium Oxide Nanopowder
- Esstech X-167-0340 Glass Ionomer Cement Liquid
- Alliance Polymers Zythane™ 7070A Thermoplastic Polyurethane Elastomer
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 40% Cold Rolled (UNS S30403)
- ExxonMobil Santoprene® 221-64W175 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved