SABIC Innovative Plastics LNP VERTON MV008SU PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON MV008SU PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* MV008SU is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.00080 cm/cm @Time 86400 sec |
0.00080 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0032 cm/cm @Time 86400 sec |
0.0032 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | ASTM D638 |
| 127 MPa | 18400 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D638 | |
| Tensile Modulus | 9.55 GPa | 1390 ksi | 50 mm/min; ASTM D638 |
| 10.12 GPa | 1468 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| 187 MPa | 27100 psi | ISO 178 | |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ASTM D790 |
| 8.25 GPa | 1200 ksi | ISO 178 | |
| Izod Impact, Notched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 46.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 82.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® MC1300 PC+ABS (Asia Pacific)
- PolyOne Geon™ Vinyl Flexible F70E Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lehmann & Voss LUVOCOM® 19-7660 Polyamide 46, with glass fiber, PTFE, lubricant modified
- Techmer ES HiFill® PEI BK
- SABIC Innovative Plastics NORYL N190 PPE+HIPS (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Thermocomp PZ006 PA 6 (Asia Pacific)
- Saint-Gobain Chemfab® 10 Tear Resistant PTFE-Coated Glass
- Wellman Wellamid® XT1486-BK Medium Impact Nylon 66
- Total PPR 3260 Random Copolymer Polypropylene, Extrusion Grade
- Tra-Con Tra-Bond 868-6N3 Room Temperature Cure Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved