SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled , Acetal Copolymer, PTFE Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D 792
1.48 g/cc
0.0535 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0075 cm/cm

@Time 86400 sec
 0.0075 in/in

@Time 24.0 hour
 ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.013 - 0.015 cm/cm

@Time 86400 sec
 0.013 - 0.015 in/in

@Time 24.0 hour
 ASTM D 955
0.014 cm/cm

@Time 86400 sec
 0.014 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
ISO 527
127 MPa
18400 psi
ASTM D 638
Tensile Strength, Yield 122 MPa
17700 psi
ISO 527
127 MPa
18400 psi
ASTM D 638
Elongation at Break 1.8 %
1.8 %
ISO 527
1.9 %
1.9 %
ASTM D 638
Elongation at Yield 1.8 %
1.8 %
ISO 527
1.9 %
1.9 %
ASTM D 638
Tensile Modulus 14.3 GPa
2070 ksi
1 mm/min; ISO 527
15.85 GPa
2299 ksi
50 mm/min; ASTM D 638
Flexural Strength 180 MPa
26100 psi
ISO 178
186 MPa
27000 psi
ASTM D 790
Flexural Modulus 12.9 GPa
1870 ksi
ISO 178
13.1 GPa
1900 ksi
ASTM D 790
Izod Impact, Notched 0.480 J/cm

@Temperature 23.0 °C
 0.899 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 5.12 J/cm

@Temperature 23.0 °C
 9.59 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 31.0 kJ/m²

@Temperature 23.0 °C
 14.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
11.0 J

@Temperature 23.0 °C
 8.11 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.36
0.36
ASTM D 3702 Modified
K (wear) Factor 127 x 10-8 mm³/N-M
63.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 34.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 18.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
34.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 19.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 159 °C
318 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
160 °C

@Thickness 3.20 mm
 320 °F

@Thickness 0.126 in
 unannealed; ASTM D 648