Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 0.765 GPa | 111 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 196 MPa | 28400 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 9.61 GPa | 1390 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.579 J/cm @Thickness 6.35 mm |
1.08 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.735 J/cm @Thickness 3.17 mm |
1.38 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C @Thickness 6.40 mm |
433 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 210 °C | 410 °F | B/50; ISO R306 |
| 212 °C | 414 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 0.750 - 3.00 mm |
V-0 @Thickness 0.0295 - 0.118 in |
Users viewing this material also viewed the following:
- Osprey Metals 316L Stainless Steel Powder (Grade 80% - 22)
- SABIC Innovative Plastics Lexan® FXM101 PC (Europe-Africa-Middle East)
- ICO Polymers ICOFLOâ„¢ 510-5069 400 Micron LLDPE Powder
- UBE UBEPOL VCR406 Synthetic Rubber (Raw Polymer)
- Westlake EC478AA Low Density Polyethylene
- Trelleborg R608 Commercial Natural Rubber Polyisoprene
- DSM Akulon® S223-HG6 (Dry) 30% Glass Reinforced Nylon 66 (North America)
- Dow Corning 2501 Cosmetic Wax
- Alliance Polymers Zythane™ 6050D Thermoplastic Polyurethane Elastomer
- DuPont Performance Polymers VESPEL TP-8929 Polyimide
Copyright © lookpolymers.com All Rights Reserved