SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* OCL32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| 119 % | 119 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1 mm/min; ISO 527 |
| 12.56 GPa | 1822 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 119 MPa | 17300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.18 GPa | 1330 ksi | 2 mm/min; ISO 178 |
| 9.20 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.45 J/cm | 6.46 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 274 °C | 525 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 274 °C @Thickness 3.20 mm |
525 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C | 453 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Permabond 268 Cyanoacrylate, General purpose
- Lubriplate AS 148 Oil Food Machinery Oil
- Garlock 8798 Neoprene Rubber Diaphragm, Nylon Insert
- Gromax BTG30-DN03N1 Nylon 6 30% Glass Filled (Dry)
- Lubrizol Advanced Materials Pearlstick® 45-90/03 Polycaprolactone based TPU
- Samyang Tribit® 1500G20 PBT, Reinforced General Purpose
- Sumitomo Bakelite North America E 9405H-1 Glass Filled Electrical Encapsulation Grade Epoxy
- A. Schulman POLYBATCH™ XAMF-500-T Process Aid Concentrate, Concentrate Based In LLDPE
- Hexcel® HexForce™ GA160 Carbon Fabric
- 3M 468MP High Performance Adhesive Transfer Tapes with Adhesive 200MP
Copyright © lookpolymers.com All Rights Reserved