SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% GR, increased strength/stiffness vs unreinforced. Non-flame retardant. For appliance handles, spotlights, electric motors, pump housings etc.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D 792 |
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 1.50 - 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0040 - 0.0050 cm/cm @Thickness 3.20 - 4.60 mm |
0.0040 - 0.0050 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0060 - 0.0090 cm/cm @Thickness 3.20 - 4.60 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D 785 |
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D 638 |
| Flexural Strength | 199 MPa | 28900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.960 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 9.61 J/cm @Temperature 23.0 °C |
18.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.0 µm/m-°C @Temperature 60.0 - 138 °C |
15.0 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 2.50e+16 ohm-cm | >= 2.50e+16 ohm-cm | ASTM D 257 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
ASTM D 150 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D 150 | |
| Dielectric Strength | 21.9 kV/mm @Thickness 3.20 mm |
556 kV/in @Thickness 0.126 in |
in air; ASTM D 149 |
| 26.4 kV/mm @Thickness 1.60 mm |
671 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 | |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
ASTM D 150 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRESEAL® TPE 5020
- Covestro Apec® 2000 Polycarbonate (discontinued **)
- Glastic 1130 Angles, Channels, and Structural Shapes
- Lanxess Durethan® BC 30 S 000000 Nylon 6
- Karina E 39/81-IE MBU Pink Color Concentrate
- LG Chemical 40 AF Flame Retardant HIPS
- DAK Americas Laser+® MB912 PET
- Azdel Plus C401B02N 40% Chopped Fiber Mat / PP Resin Matrix
- ArcelorMittal AS120 Aluminized steel
- SABIC Innovative Plastics LNP VERTON RV00CEXP PA 66 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved