SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
| 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.69 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| 9.40 GPa | 1360 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 189 MPa | 27400 psi | ISO 178 |
| 192 MPa | 27800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 193 MPa | 28000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.41 GPa | 1070 ksi | 2 mm/min; ISO 178 |
| 7.91 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.03 J/cm | 1.93 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.49 J/cm | 15.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.61 | 0.61 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D3702 Modified |
| K (wear) Factor | 6.04 x 10-8 mm³/N-M | 3.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 98.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 197 °C @Thickness 3.20 mm |
387 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Osprey Metals Ni 401 Brazing Powder
- LG Chemical SEETEC R3400 Polypropylene Random Copolymer
- SABIC Innovative Plastics LNP STAT-KON DE0049P PC (Asia Pacific)
- Borealis RJ900MO Polypropylene Random Copolymer
- BASF Basantol® 311 Red Liquid
- Arkema Group Lacovyl® S 091 PVC
- DSM Arnitel® CM622 TPC-ES
- Phillips Sumika Marlex® CHP-055 Thermoplastic Polyolefin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved