Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.77 GPa | 981 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 8.04 GPa | 1170 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 6.35 mm |
1.47 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.853 J/cm @Thickness 3.17 mm |
1.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C @Thickness 6.40 mm |
437 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 216 °C | 421 °F | B/50; ISO R306 |
| 220 °C | 428 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 0.750 - 3.00 mm |
HB @Thickness 0.0295 - 0.118 in |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 1000 E High Impact Grade Acrylic Resin
- Iran Petrochemical (PCC) MF3820 High Density Polyethylene
- Samsung Cheil Industries Starex® SF-0941 MABS, Unreinforced Scratch Resistant
- California Fine Wire Nickel Alloy 120 Nickel Iron Resistance Wire
- Ametek High Purity Nickel Strip 899A 3/4 Hard
- Colorite Polymers 2019F Rigid PVC
- Aclo Accucomp ABS ABS801V Automotive Approved Grade
- A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene
- SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Europe-Africa-Middle East)
- Hong Kun Group 4-Bromo-2-fluorobenzoic Acid Pharmaceutical Intermediate
Copyright © lookpolymers.com All Rights Reserved