Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 250 °C |
16 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Ash | 31 % | 31 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 0.824 GPa | 119 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 10.8 GPa | 1560 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.696 J/cm @Thickness 6.35 mm |
1.30 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.785 J/cm @Thickness 3.17 mm |
1.47 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C @Thickness 6.40 mm |
432 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C @Thickness 6.40 mm |
412 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 212 °C | 414 °F | B/50; ISO R306 |
| 215 °C | 419 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- MV Labs SM700 Sm(NO3)3·6H2O Samarium nitrate hexahydrate
- RedEye On Demand Polycarbonate High Impact Strength & Temperature Resistant for Rapid Prototyping
- Ravago Manufacturing Americas Hylon® N1033STL Nylon 6/6 (Cond) (discontinued **)
- Hyosung Topilene R601 PP
- Johnson Matthey Matti-phos 15 Alloy for Fluxless Brazing of Copper
- Samsung Cheil Industries Infino® TN-1100 PC, Unreinforced FR
- SABIC Innovative Plastics LNP VERTON RV00ASXP PA 66 (Europe-Africa-Middle East)
- Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- Dow ISOBIND™ 1088 Isocyanate Binder
Copyright © lookpolymers.com All Rights Reserved