SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* Noryl_HM4025 compound is a 40% Glass/Mineral filled high modulus grade. DTUL 255F (124C). UL94 V-0/V-1/5VA rated in black and gray only (see thicknesses).
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D792
Water Absorption 0.060 %

@Time 86400 sec
 0.060 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0015 cm/cm

@Thickness 3.20 mm
 0.0015 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ASTM D785
Tensile Strength at Break 127 MPa
18400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D638
Flexural Yield Strength 158 MPa
22900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 9.65 GPa
1400 ksi
2.6 mm/min, 100 mm span; ASTM D790
Poissons Ratio 0.38
0.38
ASTM E 132
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Coefficient of Friction, Static 0.42
0.42
steel; ASTM D1894
0.44
0.44
self; ASTM D1894
Taber Abrasion, mg/1000 Cycles 35
35
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.6 µm/m-°C

@Temperature -40.0 - 95.0 °C
 12.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
CTE, linear, Transverse to Flow 32.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
 18.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 123 °C

@Thickness 6.40 mm
 253 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.47 mm
 V-1

@Thickness 0.0579 in
 UL 94
V-0

@Thickness 2.99 mm
 V-0

@Thickness 0.118 in
 UL 94
5VA

@Thickness 2.51 mm
 5VA

@Thickness 0.0988 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Surface Resistance 1.00e+17 ohm
1.00e+17 ohm
ASTM D257
Dielectric Strength 25.0 kV/mm

@Thickness 1.60 mm
 635 kV/in

@Thickness 0.0630 in
 in air; ASTM D149
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A