Wellman Wellamid® MR410 22H-WBK 40% Mineral Reinforced, Weatherable Black Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® MR410 22H-WBK 40% Mineral Reinforced, Weatherable Black Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Mineral Reinforced, Weatherable Black Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183-87 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178-93 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-93 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPH4504H PPC (Europe-Africa-Middle East)
- H.C. Starck Molybdenum Alloy PBT, Bar
- SABIC Innovative Plastics ULTEM 1010FC PEI (Europe-Africa-Middle East)
- Saint-Gobain Norton® V770 Low-Density Pressure Sensitive Adhesive Sealant Foam
- Wellman Wellamid® GF43-66 XE-N 43% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
- Ensinger Tecapeek® XP-119 Compression Molded PEEK Compound, 10% Carbon Fiber
- Epoxy Technology EPO-TEK® EK2000 Epoxy
- BASF Ultramid® A3HG7 35% Glass Filled PA66 (Dry)
- DuPont Surlyn® SURSG201UG (discontinued **)
- Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched
Copyright © lookpolymers.com All Rights Reserved